EFFECT OF SILICA FUME IN THE PROPERTIES OF LIGHTWEIGHT CONCRETE WITH EXPANDED CLAY

Authors

DOI:

https://doi.org/10.29183/2447-3073.MIX2022.v8.n1.29-40

Keywords:

Lightweight concrete, Silica fume, Expanded clay, Efficiency factor

Abstract

The use of lightweight concrete (LC) represents a great challenge due to the reduction of the mechanical properties caused by the substitution of conventional aggregate for light aggregate. In view of the above, this paper aimed to verify the effect of the addition of 10% of silica fume (SF) in mixtures of concrete with replacement of 50% and 100% of the volume of crushed stone by expanded clay (EC). In the fresh state, the content of superplasticizer additive needed to obtain a consistency of 100±20 mm was analyzed using the slump test. In the hardened state, tensile and compressive strengths were analyzed at 3, 7 and 21 days of hydration. A decrease in the mechanical performance of the concrete was observed when the gravel was replaced by EC. Despite this decrease, lightweight concretes resulted in greater strength/weight ratios. It was observed that the addition of SF significantly improved the mechanical properties of lightweight concrete. Thus, it is possible to conclude that the addition of SF can compensate for the loss of mechanical performance caused by the replacement of conventional coarse aggregate with expanded clay, without the need to increase the amount of cement in the mixture

Author Biographies

Marina Costa de Souza, Centro Universitário Euro-Americano (UNIEURO)

Engenheira Civil formada pelo Centro Universitário Euro-Americano (UNIEURO).

Amália de Sousa Davi, Centro Universitário Euro-Americano (UNIEURO)

Engenheira Civil formada pelo Centro Universitário Euro-Americano (UNIEURO).

Yuri Sotero Bomfim Fraga, Centro Universitário Euro-Americano (UNIEURO)

Doutorando e mestre (2019) em Estruturas e Construção Civil pela Universidade de Brasília - UnB. Especialista em Engenharia de Segurança do Trabalho pela Universidade Candido Mendes - UCAM (2018), pós-graduando em Especialização em Engenharia de Estruturas de Concreto Armado pela Faculdade Única de Ipatinga - FUNIP, graduado em Engenharia Civil pela Universidade Tiradentes - UNIT (2016) e em Inglês pelo Fisk (2012). Possui experiência na construção, orçamento e planejamento de conjuntos habitacionais populares, edificações verticais de alto padrão e Obras de Arte Especiais - OAEs, além de atuação como docente nas disciplinas Projeto Arquitetônico, Hidráulica, Instalações Elétricas, Instalações Hidráulicas, Prevenção e Combate de Incêndio e SPDA e Materiais de Construção I e II. Em 2019 atuou como professor substituto do Departamento de Engenharia Civil e Ambiental da UnB na área de sistemas construtivos e materiais de construção e atualmente desenvolve projetos de engenharia (arquitetônico, elétrico, hidrossanitário e combate a incêndio) com auxílio dos softwares Revit, QiElétrico e QiHidrossanitário. Os principais temas de pesquisa são: materiais cimentícios suplementares, nanomateriais, concreto de alto desempenho, microestrutura do concreto e tecnologia BIM.

References

ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS, ABNT. NBR 7211 – Agregados para concreto – Especificação. Rio de Janeiro, 2009.

ANGELIN, A. F. Concreto leve estrutural - Desempenhos físicos, térmicos, mecânicos e microestruturais. 2014. p. 1-98. Dissertação (Mestrado em Tecnologia) – Tecnologia e Inovação. Universidade Estadual de Campinas, Limeira, 2014.

BONIFÁCIO, J. S. R.; GODINHO, D. S. S. Estudo do efeito das fibras de vidro e polipropileno nas propriedades mecânicas do concreto. 2015. 19 f. Trabalho de conclusão de curso (Bacharelado em Engenharia Civil) – Universidade do Extremo Sul Catarinense, Criciúma, 2015.

BORJA, E.V. Efeito da adição da argila expandida e adições minerais na formulação de concretos estruturais leves autoadensáveis. 2011. p. 1-230. Tese (Doutorado em Engenharia Mecânica) – Engenharia Mecânica. Universidade Federal do Rio Grande do Norte, Natal, 2011.

DONATO, M. Comportamento mecânico de concreto compactado com rolo reforçado com fibras de polipropileno. 2003. p. 1-82. Dissertação (Mestrado em Engenharia) – Engenharia Civil. Universidade Federal do Rio Grande do Sul, Porto Alegre, 2003.

FÉDÉRATION INTERNATIONALE DU BÉTON (FIB). Lightweigh aggregate concrete. Guidance Documents – Bulletin 8. FIB, Lousanne, Suíça, 2000.

FERNANDES, A. J. M. Influência do teor de sílica e alumina no comportamento pozolânico de materiais cimentícios suplementares. 2018. 165 f. Dissertação (Mestrado em Engenharia) – Engenharia Civil. Universidade do Vale do Rio dos Sinos, Programa de Pós-Graduação, São Leopoldo, RS, 2018.

FRAGA, Y. S. B.; RÊGO, J. H. S.; CAPUZZO, V. M. S.; ANDRADE, D. S. Efeito da ultrasonicação da sílica ativa e da nanossílica coloidal em pastas de cimento. Revista Matéria, v. 25, n.4, p. 1-16, 2020.

GOMES, P. C. C.; ALENCAR, T. F. F. De; SILVA, N. V. Da; MORAES, K. A. de M.; ANGULO, S. C. Obtenção de concreto leve utilizando agregados reciclados. Ambiente Construído, v. 15, n. 3, p. 31–46, 2015.

GUIMARÃES, J. P. F. Sinergia entre a nanosílica e a sílica ativa na produção do concreto. In: 56º Congresso Brasileiro do Concreto, 2014, Natal. Anais [...]. Natal: Ibracon, 2014.

HELENE, P., TERZIAN, P. Manual de dosagem e controle do concreto, São Paulo, PINI. SENAI., 1992.

HERMANN, A.; LANGARO, E. A.; SILVA, S. H. L.; KLEIN, N. S. Empacotamento de partículas de cimento e sílica ativa em pastas pelo uso de modelo analítico. Revista IBRACON de Estruturas e Materiais, v. 9, n. 1, p. 48–65, 2016.

LIMA, C. I. V.; COUTINHO, C. O. D.; AZEVEDO, G. G. C.; BARROS, T. Y. G.; TAUBER, T. C.; LIMA, S. F. Concreto e suas inovações. Ciências exatas e tecnológicas, p. 31–40, 2014.

KALPANA, M.; TAYU, A. Experimental investigation on lightweight concrete added with industrial waste (steel waste). Materials Today: Proceedings, v. 22. p. 887–889, 2019.

KHAN, M. N. N.; SAHA, A. K.; SARKER, P. K. Reuse of waste glass as a supplementary binder and aggregate for sustainable cement-based construction materials: A review. Journal of Building Engineering, v. 28, p. 101052, 2020.

LIMA, B. L. N.; OLIVEIRA, M. S.; OLIVEIRA, P. T.; SILVA, L. Análise do potencial da sílica ativa na resistência à compressão compressão do concreto. In: 59ª edição Congresso Brasileiro do Concreto. 2017, p. 0–11, 2018.

MAYCÁ, Jefferson.; CREMONINI, Ruy A.; RECENA, Fernando A. P. Conctribuição ao estudo da argila expandida nacional como alternativa de agregado graúdo para concretos leves estruturais (CLE). 2018.

MEHTA, P.K.; MONTEIRO, P.J.M. Concreto: Microestrutura, Propriedades e Materiais. 1ª Edição, São Paulo, IBRACON, 2008.

MO, K. H.; LEE, H. J.; LIU, M. Y. J.; LING, T. C. Incorporation of expanded vermiculite lightweight aggregate in cement mortar. Construction and Building Materials, v. 179, p. 302–306, 2018.

MO, K. H.; LING, T. C.; ALENGARAM, U. J.; YAP, S. P.; YUEN, C. W. Overview of supplementary cementitious materials usage in lightweight aggregate concrete. Construction and Building Materials, v. 139, p. 403–418, 2017.

MORAVIA, W. G; GUMIERI, A. G.; VASCONCELOS, W. L. Efficiency factor and modulus of elasticity of lightweight concrete with expanded clay aggregate. Revista IBRACON de Estruturas e Materiais. São Paulo, v. 3, n. 2, p. 195–204, junho de 2010.

MORAVIA, W. G.; OLIVEIRA, C. A. S.; GUMIERI, A. G.; VASCONCELOS, W. L. Caracterização microestrutural da argila expandida para aplica̧ão como agregado em concreto estrutural leve. Ceramica, v. 52, n. 322, p.193–199, 2006.

REVILLA-CUESTA, V.; SKAF, M.; FALESCHINI, F.; MANSO, J. M.; ORTEGA-LÓPEZ, V. Self-compacting concrete manufactured with recycled concrete aggregate: An overview. Journal of Cleaner Production, v. 262, p. 1-19, 2020.

ROMANO, R. C. O.; SCHREURS, H.; JOHN, V. M.; PILEGGI, R. G. Influência da técnica de dispersão nas propriedades de sílica ativa. Ceramica, v. 54, n. 332, p. 456–461, 2008.

ROSSIGNOLO, J. A.; OLIVEIRA, I. L. Concreto leve estrutural com metacaulim. Revista Minerva. v. 3, n. 2, p. 177–187, 2005.

ROSSIGNOLO, J. A.; OLIVEIRA, I. L. Efeito do Metacaulim nas propriedades do concreto leve estrutural. Acta Scientiarum - Technology, v.29, 2007.

ROSSIGNOLO, J. A. Concreto leve estrutural: produção, propriedades, microestrutura e aplicações. 1 ed. São Paulo: PINI, 2009.

ROSSIGNOLO, J. A. Concreto leve de alto desempenho modificado com SB para pré-fabricados esbeltos – Dosagem, produção, propriedades e mocroestrutura. 2003. p. 1-211. Tese (Doutorado em Interunidades em Ciência e Engenharia de Materiais) – Engenharia Civil, Universidade de São Paulo, São Paulo, 2003.

ROSSIGNOLO, J. A.; Oliveira, I. L. Efeito do Metacaulim nas propriedades do concreto leve estrutural. Acta Scientiarum - Technology, v.29, 2007.

SACHT, H. M.; ROSSIGNOLO, J. A.; SANTOS, W. N. Avaliação da condutividade térmica de concretos leves com argila expandida. Revista Materia, v. 15, n. 1, p. 031–039, 2010.

SCOBAR, R. L. Concreto leve estrutural: substituição do agregado graúdo convencional por argila expandida. 45p. Trabalho de Conclusão de Curso (Bacharelado) - Universidade Tecnológica Federal do Paraná. Campo Mourão, 2016.

SILVA, H. H. A. B. Caracterização mineralógica e filiação da vermiculita da Mina Cerrado III - Sanclerlândia-GO. 2006. p. 1-127. Dissertação (Mestrado em Geologia) - Mineralogia e Petrologia, Universidade de Brasília, Brasília, 2006.

SOUSA, I. P. S. Obtenção de nanossílica funcionalizada visando o uso como aditivo em misturas cimentícias. 2017. 72 f. Dissertação (Mestrado em Química) – Universidade Federal de Goiás, Goniânia, 2017.

STOCCO, W.; RODRIGUES, D.; CASTRO, A.P.A.S. Concreto leve com uso de EPS. Cobenge 2009. n. 81, p. 1129-1134, 2009.

SUTCU, M. Influence of expanded vermiculite on physical properties and thermal conductivity of clay bricks. Ceramics International, v. 41, n. 2, p. 2819–2827, 2015.

TUTIKIAN, B. F.; HELENE, P. Dosagem dos Concretos de Cimento Portland. Concreto: Ciência e Tecnologia. São Paulo. Ibracon, 2011, cap 12.

UGARTE J. F. O, SAMPAIO J. A, FRANÇA S. C. A. Vermiculita. In: Rochas & Minerais Industriais: Usos e Epecificações. Rio de Janeiro: CETEM, 2008. Cap 38. p.866-887.

VASKE, N. R.; CAMPAGNOLO, J. L.; DAL MOLIN, D. C. C. Relationship between the compressive strength of silica fume mortar applied to the substratum and the one obtained in standardized cylindrical test specimens. Revista IBRACON de Estruturas e Materiais, v. 3, n. 3, p. 322–345, 2010.

Downloads

Published

2021-12-01

How to Cite

Souza, M. C. de, Davi, A. de S., & Fraga, Y. S. B. (2021). EFFECT OF SILICA FUME IN THE PROPERTIES OF LIGHTWEIGHT CONCRETE WITH EXPANDED CLAY. ix Sustentável, 8(1), 29–40. https://doi.org/10.29183/2447-3073.MIX2022.v8.n1.29-40

Issue

Vol. 8 No. 1 (2022): Mix Sustentável (edição regular)

Section

Científica

License

Creative Commons Copyright Notice

Attribution 4.0 International